Fretting

Abstract: Young's modulus as well as tensile strength, ductility, fatigue life, fretting fatigue life, wear properties, functionalities, etc., should be adjusted to levels that are suitable for structural biomaterials used in implants that replace hard tissue. These factors may be collectively referred to as mechanical biocompatibilities. In this paper, the following are described with regard to biomedical applications of titanium alloys: the Young's modulus, wear properties, notch fatigue strength, fatigue behaviour on relation to ageing treatment, improvement of fatigue strength, fatigue crack propagation resistance and ductility by the deformation-induced martensitic transformation of the unstable beta phase, and multifunctional deformation behaviours of titanium alloys.

Abstract: In situ degradation of metal-alloy implants is undesirable for two reasons: the degradation process may decrease the structural integrity of the implant, and the release of degradation products may elicit an adverse biological reaction in the host Degradation may result from electrochemical dissolution phenomena, wear, or a synergistic combination of the two Electrochemical processes may include generalized corrosion, uniformly affecting the entire surface of the implant, and localized corrosion, affecting either regions of the device that are shielded from the tissue fluids (crevice corrosion) or seemingly random sites on the surface (pitting corrosion) Electrochemical and mechanical processes (for example, stress corrosion cracking, corrosion fatigue, and fretting corrosion) may interact, causing premature structural failure and accelerated release of metal particles and ions The clinical importance of degradation of metal implants is evidenced by particulate corrosion and wear products in tissue surrounding the implant, which may ultimately result in a cascade of events leading to periprosthetic bone loss Furthermore, many authors have reported increased concentrations of local and systemic trace metal in association with metal implants1,4,5,9-11,14,18,25,26,28,29,47,49-55,58,71,72,75-77,87,90,108-110 There also is a low but finite prevalence of corrosion-related fracture of the implant This review focuses on electrochemical corrosion phenomena in alloys used for orthopaedic implants A summary of basic electrochemistry is followed by a discussion of retrieval studies of the response of the implant to the host environment and the response of local tissue to implant corrosion products The systemic implications of the release of metal particles also are presented Finally, future directions in biomaterials research and development …

Abstract: A new theory for wear of metals is considered. The theory is based on the behavior of dislocations at the surface, sub-surface crack and void formation, and subsequent joining of cracks by shear deformation of the surface. The proposed theory predicts qualitatively that the wear particle shape is likely to be thin flake-like sheets and that the surface layer can undergo large plastic deformation. It also predicts a number of experimentally observed phenomena such as the difference in wear particle sizes and the dependence of fretting wear rate on displacement amplitude. All theoretical predictions are supported by experimental evidences. A wear equation is developed based on the proposed theory.