Epitaxy

Abstract: Atmospheric pressure metalorganic vapor phase epitaxial growth and characterization of high quality GaN on sapphire (0001) substrates are reported. Using AlN buffer layers, GaN thin films with optically flat surfaces free from cracks are successfully grown. The narrowest x‐ray rocking curve from the (0006) plane is 2.70’ and from the (2024) plane is 1.86’. Photoluminescence spectra show strong near band edge emission. The growth condition dependence of crystalline quality is also studied.

Abstract: Semiconductor heterostructures with modulated composition and/or doping enable passivation of interfaces and the generation of devices with diverse functions. In this regard, the control of interfaces in nanoscale building blocks with high surface area will be increasingly important in the assembly of electronic and photonic devices. Core-shell heterostructures formed by the growth of crystalline overlayers on nanocrystals offer enhanced emission efficiency, important for various applications. Axial heterostructures have also been formed by a one-dimensional modulation of nanowire composition and doping. However, modulation of the radial composition and doping in nanowire structures has received much less attention than planar and nanocrystal systems. Here we synthesize silicon and germanium core-shell and multishell nanowire heterostructures using a chemical vapour deposition method applicable to a variety of nanoscale materials. Our investigations of the growth of boron-doped silicon shells on intrinsic silicon and silicon-silicon oxide core-shell nanowires indicate that homoepitaxy can be achieved at relatively low temperatures on clean silicon. We also demonstrate the possibility of heteroepitaxial growth of crystalline germanium-silicon and silicon-germanium core-shell structures, in which band-offsets drive hole injection into either germanium core or shell regions. Our synthesis of core-multishell structures, including a high-performance coaxially gated field-effect transistor, indicates the general potential of radial heterostructure growth for the development of nanowire-based devices.

Abstract: We report a demonstration of single-crystal gallium oxide (Ga2O3) metal-semiconductor field-effect transistors (MESFETs). A Sn-doped Ga2O3 layer was grown on a semi-insulating β-Ga2O3 (010) substrate by molecular-beam epitaxy. We fabricated a circular MESFET with a gate length of 4 μm and a source–drain spacing of 20 μm. The device showed an ideal transistor action represented by the drain current modulation due to the gate voltage (VGS) swing. A complete drain current pinch-off characteristic was also obtained for VGS < −20 V, and the three-terminal off-state breakdown voltage was over 250 V. A low drain leakage current of 3 μA at the off-state led to a high on/off drain current ratio of about 10 000. These device characteristics obtained at the early stage indicate the great potential of Ga2O3-based electrical devices for future power device applications.

Abstract: We propose a widegap II–VI semiconductor alloy, MgxZn1−xO, for the fabrication of heteroepitaxial ultraviolet light emitting devices based on ZnO. The c-axis oriented MgxZn1−xO films were epitaxially grown by pulsed laser deposition on ZnO epitaxial films and sapphire (0001) substrates using ceramic targets. Solid solution films were prepared with Mg content up to x=0.33, achieving a band gap of 3.99 eV at room temperature. MgO impurity phase segregated at x⩾0.36. Lattice constants of MgxZn1−xO films changed slightly (∼1%), increasing in a axis and decreasing in c-axis direction with increasing x. These films showed ultraviolet photoluminescence at energies from 3.36 (x=0) to 3.87 eV (x=0.33) at 4.2 K.