Crystallization

Abstract: Uniform, spherical-shaped TiO2:Eu nanoparticles with different doping concentrations have been synthesized through controlled hydrolysis of titanium tetrabutoxide under appropriate pH and temperature in the presence of EuCl3·6H2O. Through air annealing at 500°C for 2 h, the amorphous, as-grown nanoparticles could be converted to a pure anatase phase. The morphology, structural, and optical properties of the annealed nanostructures were studied using X-ray diffraction, scanning electron microscopy, energy-dispersive X-ray spectroscopy [EDS], and UV-Visible diffuse reflectance spectroscopy techniques. Optoelectronic behaviors of the nanostructures were studied using micro-Raman and photoluminescence [PL] spectroscopies at room temperature. EDS results confirmed a systematic increase of Eu content in the as-prepared samples with the increase of nominal europium content in the reaction solution. With the increasing dopant concentration, crystallinity and crystallite size of the titania particles decreased gradually. Incorporation of europium in the titania particles induced a structural deformation and a blueshift of their absorption edge. While the room-temperature PL emission of the as-grown samples is dominated by the 5D0 - 7Fj transition of Eu+3 ions, the emission intensity reduced drastically after thermal annealing due to outwards segregation of dopant ions.

Abstract: We report on the properties of one example of a new family of metallic alloys which exhibit excellent glass forming ability. The critical cooling rate to retain the glassy phase is of the order of 10 K/s or less. Large samples in the form of rods ranging up to 14 mm in diameter have been prepared by casting in silica containers. The undercooled liquid alloy has been studied over a wide range of temperatures between the glass transition temperature and the thermodynamic melting point of the equilibrium crystalline alloy using scanning calorimetry. Crystallization of the material has been studied. Some characteristic properties of the new material are presented. The origins of exceptional glass forming ability of these new alloys are discussed.

Abstract: The following article is based on the MRS Medal talk presented by William L. Johnson at the 1998 MRS Fall Meeting on December 2, 1998. The MRS Medal is awarded for a specific outstanding recent discovery or advancement that has a major impact on the progress of a materials-related field. Johnson received the honor for his development of bulk metallic glass-forming alloys, the fundamental understanding of the thermodynamics and kinetics that control glass formation and crystallization of glass-forming liquids, and the application of these materials in engineering.The development of bulk glass-forming metallic alloys has led to interesting advances in the science of liquid metals. This article begins with brief remarks about the history and background of the field, then follows with a discussion of multicomponent glass-forming alloys and deep eutectics, the chemical constitution of these new alloys, and how they differ from metallic glasses of a decade ago or earlier. Recent studies of deeply undercooled liquid alloys and the insights made possible by their exceptional stability with respect to crystallization will then be discussed. Advances in this area will be illustrated by several examples. The article then describes some of the physical and specific mechanical properties of bulk metallic glasses (BMGs), and concludes with some interesting potential applications.The first liquid-metal alloy vitrified by cooling from the molten state to the glass transition was Au-Si, as reported by Duwez at Caltech in 1960. Duwez made this discovery as a result of developing rapid quenching techniques for chilling metallic liquids at very high rates of 105–106 K/s.

Abstract: We report that crystalline phases with ferroelectric behavior can be formed in thin films of SiO2 doped hafnium oxide. Films with a thickness of 10 nm and with less than 4 mol. % of SiO2 crystallize in a monoclinic/tetragonal phase mixture. We observed that the formation of the monoclinic phase is inhibited if crystallization occurs under mechanical encapsulation and an orthorhombic phase is obtained. This phase shows a distinct piezoelectric response, while polarization measurements exhibit a remanent polarization above 10 μC/cm2 at a coercive field of 1 MV/cm, suggesting that this phase is ferroelectric. Ferroelectric hafnium oxide is ideally suited for ferroelectric field effect transistors and capacitors due to its excellent compatibility to silicon technology.