Comproportionation

Abstract: Manganese oxides function as efficient electrocatalysts for water oxidation to molecular oxygen in strongly alkaline conditions, but are inefficient at neutral pH. To provide new insight into the mechanism underlying the pH-dependent activity of the electrooxidation reaction, we performed UV-vis spectroelectrochemical detection of the intermediate species for water oxidation by a manganese oxide electrode. Layered manganese oxide nanoparticles, δ-MnO(2) (K(0.17)[Mn(4+)(0.90)Mn(3+)(0.07)□(0.03)]O(2)·0.53H(2)O) deposited on fluorine-doped tin oxide electrodes were shown to catalyze water oxidation at pH from 4 to 13. At this pH range, a sharp rise in absorption at 510 nm was observed with a concomitant increase of anodic current for O(2) evolution. Using pyrophosphate as a probe molecule, the 510 nm absorption was attributable to Mn(3+) on the surface of δ-MnO(2). The onset potential of the water oxidation current was constant at approximately 1.5 V vs SHE from pH 4 to pH 8, but sharply shifted to negative at pH > 8. Strikingly, this behavior was well reproduced by the pH dependence of the onset of 510 nm absorption, indicating that Mn(3+) acts as the precursor of water oxidation. Mn(3+) is unstable at pH < 9 due to the disproportionation reaction resulting in the formation of Mn(2+) and Mn(4+), whereas it is effectively stabilized by the comproportionation of Mn(2+) and Mn(4+) in alkaline conditions. Thus, the low activity of manganese oxides for water oxidation under neutral conditions is most likely due to the inherent instability of Mn(3+), whose accumulation at the surface of catalysts requires the electrochemical oxidation of Mn(2+) at a potential of approximately 1.4 V. This new model suggests that the control of the disproportionation and comproportionation efficiencies of Mn(3+) is essential for the development of Mn catalysts that afford water oxidation with a small overpotential at neutral pH.

Abstract: An integrated approach to the control of ΔE1/2 values, and therefore comproportionation equilibria, through medium effects was delineated for multi-step redox reactions involving cationic products. ΔE1/2 values (defined as E1/22+/1+ − E1/21+/0) of the two one-electron oxidations of bis(fulvalene)dinickel, 1, were measured under 45 different conditions of solvent and supporting electrolyte. The smallest value, 212 mV, was found in anisole/0.1 M [NBu4]Cl and the largest, 850 mV, in CH2Cl2/0.02 M Na[B(C6H3(CF3)2)4]. By systematically changing the solvent properties, the degree of ion-pairing strengths of the supporting electrolyte ions, and the concentration of the electrolytes, a set of ideal properties was found for maximizing ΔE1/2 values involving positively charged electrode products. Most importantly (i) the solvent must be of lower polarity and low donor strength and (ii) the supporting electrolyte must have a weakly coordinating anion (WCA). The contrast in ion-pairing tendencies of 12+ with WCAs (on...

Abstract: The ability of the terpyridine ligand to stabilize alkyl complexes of nickel has been central in obtaining a fundamental understanding of the key processes involved in alkyl−alkyl cross-coupling reactions. Here, mechanistic studies using isotopically labeled (TMEDA)NiMe2 (TMEDA = N,N,N‘,N‘-tetramethylethylenediamine) have shown that an important catalyst in alkyl−alkyl cross-coupling reactions, (tpy‘)NiMe (2b, tpy‘ = 4,4‘,4‘ ‘-tri-tert-butylterpyridine), is not produced via a mechanism that involves the formation of methyl radicals. Instead, it is proposed that (terpyridine)NiMe complexes arise via a comproportionation reaction between a Ni(II)−dimethyl species and a Ni(0) fragment in solution upon addition of a terpyridine ligand to (TMEDA)NiMe2. EPR and DFT studies on the paramagnetic (terpyridine)NiMe (2a) both suggest that the unpaired electron resides heavily on the terpyridine ligand and that the proper electronic description of this nickel complex is a Ni(II)−methyl cation bound to a reduced terpyr...

Abstract: Electrodeposited manganese oxide films (MnOx) are promising stable oxygen evolution catalysts. They are able to catalyze the oxygen evolution reaction in acidic solutions but with only modest activity when prepared by constant anodic potential deposition. We now show that the performance of these catalysts is improved when they are “activated” by potential cycling protocols, as measured by Tafel analysis (where lower slope is better): upon activation the Tafel slope decreases from ∼120 to ∼70 mV/decade in neutral conditions and from ∼650 to ∼90 mV/decade in acidic solutions. Electrochemical, spectroscopic, and structural methods were employed to study the activation process and support a mechanism where the original birnessite-like MnOx (δ-MnO2) undergoes a phase change, induced by comproportionation with cathodically generated Mn(OH)2, to a hausmannite-like intermediate (α-Mn3O4). Subsequent anodic conditioning from voltage cycling or water oxidation produces a disordered birnessite-like phase, which is ...