Fracture Behavior of Crack-Damaged Concrete Beams Reinforced with Ultra-High-Performance Concrete Layers

TL;DR: This study investigates the fracture behavior of crack-damaged concrete beams reinforced with ultra-high-performance concrete (UHPC) layers, demonstrating enhanced load-carrying capacity and crack resistance, with optimal performance achieved at specific layer thicknesses and fiber contents.

Abstract: Reinforcing crack-damaged concrete structures with ultra-high-performance concrete (UHPC) proves to be more time-, labor-, and cost-efficient than demolishing and rebuilding under the dual-carbon strategy. In this study, the extended finite element method (XFEM) in ABAQUS was first employed to develop a numerical model of UHPC-reinforced single-notched concrete (U+SNC) beams, analyze their crack extension behavior, and obtain the parameters necessary for calculating fracture toughness. Subsequently, the fracture toughness and instability toughness of U+SNC were calculated using the improved double K fracture criterion. The effects of varying crack height ratios (a/h) of SNC, layer thicknesses (d) of UHPC reinforcement, and fiber contents in UHPC (VSF) on the fracture properties of U+SNC beams were comprehensively investigated. The results indicate that (1) the UHPC reinforcement layer significantly enhances the load-carrying capacity and crack resistance of the U+SNC beams. Crack extension in the reinforced beams occurs more slowly than in the unreinforced beams; |(2) the fracture performance of the U+BNC beams increases exponentially with d. Considering both the reinforcement effect benefit and beam deadweight, the optimal cost-effective performance is achieved when d is 20 mm; (3) with constant d, increasing a/h favors the reinforcement effect of UHPC on the beams; (4) as VSF increases, the crack extension stage in the U+BNC beam becomes more gradual, with higher toughness and flexural properties; therefore, the best mechanical properties are achieved at a VSF of 3%.