Study on corona-resistance of polyimide-nano inorganic composites
Zhang Peihong,Zhang Weiguo,Liu Yan,Fan Yong,Lei Qingquan +4 more
- 01 Jun 2003
TL;DR: In this paper, a testing apparatus for voltage endurance of polyimide film materials subjected to partial discharges on its surface was developed according to IEC-343 and ASTM-2275.
24
Conduction Current Characteristics and Carrier Mobility of Both Original and Corona-Resistant Polyimide Films
TL;DR: In this paper, the electric conduction current characteristics of both Dupont original and corona resistant polyimide films (100 HN and 100 CR) before and after corona-aging eight hours under electric field of 10 kV/mm and 20 kV /mm were measured.
11
Auto-separating peaks method of TSC-curves in pet film
Xu Lei,Jiang Xiaojuan,Wang Xuan,Fan Yong,Lei Qingquan +4 more
- 01 Jun 2003
TL;DR: In this paper, two sharp peaks are obtained by auto-separating the thermally stimulated process curve ranging from 300K to 400K in PET film sample, and compared them with two peaks received by thermo-resolving method, it can be seen clearly that the data responsible for two peaks, including peak current and temperature, frequency factor, activation energy and dynamic order, is almost the same.
1
Effects of inorganic content and morphology between phases on structure and properties of the hybrid polyimide film
Zhong Jinghe,Zhang Mingyan,Jiang Qibin,Cai Binfen,Fan Yong +4 more
- 01 Jan 2005
TL;DR: In this article, a type of nano-hybrid polyimide/silica film was prepared by hydrolysis and condensation of methyl-triethoxysilane that served as the precursor of the inorganic moiety and produced the nanoparticle of silica, in-situ, in the polyamic acid solution through a sol-gel reaction.
1
The study on conductivity and electrorheology of polyacene quinone radical polymer dispersion
Fan Yong,Zheng Wei,Feng Xuebing,Lei Qingquan +3 more
- 25 Sep 1996
TL;DR: In this paper, the conductivity and electrorheological properties of semiconducting polyacene quinone radical (PAQR) polymer dispersion in silicon oil were investigated and the current-voltage curve and torque (shear stress) voltage curve both confirmed the power law under scale assumption.