Ding Guo is an academic researcher from Wuhan University of Science and Technology. The author has contributed to research in topics: Sintering & Molten salt. The author has an hindex of 3, co-authored 5 publications.
Chat about Author
Papers
Preparation and application of ZrC-coated flake graphite for Al2O3-C refractories
TL;DR: In this paper, ZrC-coated flake graphite was prepared by molten salt synthesis and added to the Al2O3-C refractory, and the effects of the molar ratio of Zr/C and the graphite particle size on ZrCo-Co-coating graphite were investigated.
52
Low-temperature synthesis of nanocrystalline ZrC coatings on flake graphite by molten salts
TL;DR: In this article, a novel molten salt synthetic route has been developed to prepare nanocrystalline zirconium carbide (ZrC) coatings on flake graphite at 900°C, using Zr powder and graphite as the source materials in a static argon atmosphere, along with molten salts as the media.
49
Novel preparation of a porous composite insulating scaffold from forsterite and sodium carbonate media
TL;DR: In this paper, forsterite, salt (Na2CO3), and phenolic resin (P resin) were used for sintering at 900 to 1 100 °C for 10 h, and the results showed that the changes in temperature did not significantly affect the phases present in the samples.
11
Effects of Concentrations of NaCl on the Sintering and Thermal Conductivity of Forsterite
TL;DR: In this article, the effects of NaCl on the sintering of forsterite as well as the thermal conductivity of the products were investigated, and it was shown that the higher the salt content in the sample, the lower the thermal properties of the sample.
2
Reaction and Sintering Mechanism of Forsterite Lightweight Material in Sodium Carbonate Molten Salt
TL;DR: In this paper, the reaction between forsterite and Na2CO3 and sintering mechanism of forsterites were studied in the presence of Na2MgSiO4 phase.
2