Andreas Schubert is an academic researcher from Audi. The author has contributed to research in topics: Aluminium & Casting (metalworking). The author has an hindex of 3, co-authored 7 publications.
Chat about Author
Papers
Patent
Aluminum alloy, useful to produce cast component and for casting components of car, comprises silicon, manganese, magnesium, copper and iron, and aluminum and production related impurities
Marc Hummel,Andreas Schubert,Manfred Dr.-Ing. Sindel +2 more
- 11 Sep 2008
TL;DR: In this paper, a process for producing cast components, preferably from the aluminum alloy, comprising subjecting the cast components after a casting process, to a solution heat treatment process and subsequently to separation process, where the separation is carried out in at least two stages.
9
Patent
Producing thin-walled metal components of a motor vehicle, comprises solution-annealing the components in a two-stage heat treatment process after its shaping and then artificial ageing after resulted deterrence
Marc Hummel,Andreas Schubert +1 more
- 08 Nov 2008
TL;DR: In this article, a two-stage solution-annealing method was proposed for a metal component with wall strength of 1.5-10 mm and the shaping of the metal component is carried out by die casting, sand casting or mold casting.
7
Patent
Joining casting to hollow profile in vehicle construction, forms keying undercuts in profile then seals its cavity to limit penetration of cast material
Marc Hummel,Andreas Schubert +1 more
- 10 Oct 2008
TL;DR: One or more undercut sections (5) are provided in the hollow profile component (1) to provide keying for the casting, and casting material flows around the undercut sections, forming a solid joint between the components as discussed by the authors.
7
Continuous Powder Extrusion for Fabrication of Carbon Fibre Reinforced Aluminium
TL;DR: In this article, the effect of the prechamber length on the mechanical properties of short fiber reinforced aluminium was examined using light microscopy. And the results showed that an extension of the Prechamber enhances the Young's modulus and the elongation of fracture due to reduced fibre fracture and better fibre alignment.
3
Patent
Aluminum-silicon die casting alloy comprises a specific amount of silicon, zinc, magnesium, manganese, zirconium, contaminants, and aluminum
Marc Hummel,Andreas Schubert,Steffen Otterbach +2 more
- 15 Feb 2013
TL;DR: In this article, an independent claim is also included for preparing a die casting component, preferably thin-walled bodywork or a chassis cast component, comprising casting a cast component with evacuated permanent molds made of the aluminum-silicon die casting alloy, and subjecting the cast component to (a) T5 heat treatment, which includes a hot exposure of the cast components at 220[deg] C for 2 hours, (b) T6 heat treatment (T6) for 1 hour, quenching in air, and hot exposure at 210[degree] C