A. Caneiro
British Hospital
16 Papers
111 Citations
A. Caneiro is an academic researcher from British Hospital. The author has contributed to research in topics: Superconductivity & Magnetization. The author has an hindex of 6, co-authored 16 publications.
Chat about Author
Papers
High temperature thermodynamic properties, orthorhombic/tetragonal transition and phase stability of GdBa2Cu3Oy and related R123 compounds
TL;DR: In this paper, thermogravimetric measurements of the equilibrium oxygen partial pressure (p(O 2 )) as a function of temperature and oxygen content have been made on GdBa 2 Cu 3 O y (Gd123) within the range 3×10 −4 atm≤ p (O 2 )≤ 1 atm and 450°C≤ T ≤ 800°C.
26
Synthesis method, control of cationic composition and superconducting behavior of Nd1.85Ce0.15Cu1±δOy
TL;DR: In this article, samples of Nd 185 Ce 015 Cu 1 ± ° O y (099 ¾ ± δ ⩽ 102) were prepared by a solid-state reaction (SSR), nitrate-decomposition method (NDM) and liquid-mix method (LMM) and characterized by XRD, SEM, EPMA, DTA and DC magnetization.
20
Crystallization of iron phosphate glasses containing up to 19 wt.% UO2.67
C.J.R. González Oliver,F.C. Lovey,A. Caneiro,D. O. Russo,D.S. Rodríguez,Flavio Soldera,J.E. Fiscina,J. Ma. Rincón +7 more
TL;DR: In this paper, the Tg-T SOFT values were obtained for glasses AR6 (main components: 57.3% P 2 O 5. 18.4% Fe 2 O 3, 6.2-18.5% UO 2.67 ).
19
Thermogravimetric study of the reduction step in Nd1.85Ce0.15Cu1.01Oy as a function of the oxygen partial pressure
TL;DR: In this article, the superconducting transition of samples with controlled oxygen content was studied through Magnetically Modulated Microwave Absorption (MaMMA), and it was observed only for samples quenched at PO2 lower than 1.4 × 10−2 atm.
17
Copper content and superconductivity of Nd1.85Ce0.15Cu1+δOy
TL;DR: In this paper, the superconducting transition of Nd 1.85 Ce 0.15 Cu 1+δ O y samples was studied as a function of the Cu content and processing temperature through magnetic modulated microwave absorption and dc magnetization measurements.
13